ONE FOR ALL MULTI-LAYER
ONE FOR ALL MULTI-LAYER
5-Layers
[1100 MPa / 47% translucency]
INFORMATION
Multilayered High Aesthetic Zirconia (HAZ) 1100MPa / 47% Translucency
ONE FOR ALL is a very strong, “4Y” zirconia that Talladium formulated to satisfy our customer's desire to have ONE zirconia for ALL indications and be aesthetic enough for anterior applications. ONE FOR ALL maintains excellent translucency with a higher more natural value (brightness) than some anterior zirconias. ONE FOR ALL is strong enough for full arch frameworks and Hybrid Screw-Retained Denture cases, abutments and full contour cases with .5mm or greater clearance.
ONE FOR ALL zirconia infiltrated with Talladium’s NEW ONE FOR ALL water-based coloring liquid, then glazed with Talladium’s NEW One For All, Fluorescence Glaze Paste.
ONE FOR ALL
[1100 MPa / 47% translucency]
INFORMATION
High Aesthetic Zirconia (HAZ) 1100MPa / 47% Translucency
ONE FOR ALL is a very strong, “4Y” zirconia that Talladium formulated to satisfy our customer's desire to have ONE zirconia for ALL indications and be aesthetic enough for anterior applications. ONE FOR ALL maintains excellent translucency with a higher more natural value (brightness) than some anterior zirconias. ONE FOR ALL is strong enough for full arch frameworks and Hybrid Screw-Retained Denture cases, abutments and full contour cases with .5mm or greater clearance. ONE FOR ALL has a CTE that is compatible with traditional zirconia porcelains and glazes.
Photo above is ONE FOR ALL zirconia infiltrated with Talladium’s NEW ONE FOR ALL water-based coloring liquid, then glazed with Talladium’s NEW One For All, Fluorescence Glaze Paste.
AT MULTI-LAYER ZIRCONIA
3 LAYER ANTERIOR TRANSLUCENT ZIRCONIA
Anterior Multilayer Zirconia [750 MPa / 49% translucency]
Talladium’s Multi-layer Pre-shaded Zirconia
Why order copings and build porcelain? This is an all-around CAD/CAM solution for the Dentist that wants Porcelain aesthetics at a zirconia price.
AT MULTI-LAYER is a pre-shaded “5Y” zirconia with multiple translucencies therefore the color layer won’t “white out” during seating adjustments. AT MULTI-LAYER color transitions from gingival color to incisal translucency with aesthetics that easily rival layered porcelain.
AT MULTI-LAYER is indicated for: 1.5 mm occlusal thickness, 1mm wall thickness in the posterior, up to 2 pontic spans and .7 thickness in the anterior region.
HT ZIRCONIA
(1200 MPa / 45% Translucency)
High Translucent Zirconia (HT): This formulation is a “3Y” zirconia and all around “work-horse” from our Luminesse zirconia line. We manufactured our HT Zirconia to be strong while still allowing for pleasing aesthetics.
Indications are ideal for:
Frameworks & Cutbacks with Zirconia linguals/occlusals
Bruxism Patients
Limited Clearance Cases
Long Span Pontic Frameworks
Full Arch Hybrid Screw Retained Denture Cases (with Pink Tissue)
Maryland bridges
Abutments
Masking out dark stumps, amalgams, metal post/cores.
AT ZIRCONIA
(750 MPa / 50% Translucency)
Anterior Translucent Zirconia (AT) is from Talladium’s High Aesthetic Zirconia (HAZ) Line. AT is a “5Y” zirconia designed for aesthetic cases in the anterior region in low function. AT is very translucent similar to that of Lithium Silicate yet being slightly lower in value due to its high translucency. AT Zirconia is indicated for:
Anterior single unit full contour crowns or copings.
Frameworks and full contour bridges up to 2 unit pontic spans in the anterior or 1 pontic span posterior bridges.
Anterior cases with .7 mm bite clearance or posterior units with 1.0 mm wall thickness and 1.5 mm occlusal clearance with shoulder or chamfer margins.
TMCilicate
CAD CAM silicate block, milled ceramic
TMC offers this High Aesthetic All-Ceramic in High Translucent (HT) Shades Ideal For Veneers and Inlays in: HT BL1, BL2, BL3, A1, A2, A3, A3.5, B1, B2.
Recommended for Full Contour and Cutback Cases TMC Offers Low Translucent (LT)Shades in: LT BL1, BL2, A1, A2, A3, A3.5, B1, B2, C1, C2, D2,
Available in blue block unfinished, crystalized unfinished, crystalized glazed finished.
Technical Specifications:
Density = 2.3 to 2.6 g/cm3
CTE @ 500C = 8.5 to 11.0 x 10-6K-1
Flexural Strength = 400 to 460 MPa
Vickers Hardness = 5400 MPa
Solubility after sintering <100ug/cm2